Effect of Co doping on the structural, optical and magnetic properties of ZnO nanoparticles
J Hays1, K M Reddy, N Y Graces
1Department of Physics, Boise State University, Boise, ID 83725-1570, USA.
Abstract:
We report the results of a detailed investigation of sol-gel-synthesized nanoscale Zn(1-x)Co(x)O powders processed at 350 °C with 0≤x≤0.12 to understand how the structural, morphological, optical and magnetic properties of ZnO are modified by Co doping, in addition to searching for the theoretically predicted ferromagnetism. With x increasing to 0.03, both lattice parameters a and c of the hexagonal ZnO decreased, suggesting substitutional doping of Co at the tetrahedral Zn(2+) sites. For x>0.03, these trends reversed and the lattice showed a gradual expansion as x approached 0.12, probably due to additional interstitial incorporation of Co. Raman spectroscopy measurements showed a rapid change in the ZnO peak positions for x>0.03, suggesting significant disorder and changes in the ZnO structure, in support of additional interstitial Co doping possibility. Combined x-ray photoelectron spectroscopy (XPS), electron paramagnetic resonance spectroscopy, photoluminescence spectroscopy and diffuse reflectance spectroscopy showed clear evidence for tetrahedrally coordinated high-spin Co(2+) ions occupying the lattice sites of ZnO host system, which became saturated for x>0.03. Magnetic measurements showed a paramagnetic behaviour in Zn(1-x)Co(x)O with increasing antiferromagnetic interactions as x increased to 0.10. Surprisingly, a weak ferromagnetic behaviour was observed for the sample with x = 0.12 with a characteristic hysteresis loop showing a coercivity H(c)∼350 Oe, 25% remanence M(r), a low saturation magnetization M(s)∼0.04 emu g(-1) and with a Curie temperature T(c)∼540 K. The XPS data collected from Zn(1-x)Co(x)O samples showed a gradual increase in the oxygen concentration, changing the oxygen-deficient undoped ZnO to an excess oxygen state for x = 0.12. This indicates that such high Co concentrations and appropriate oxygen stoichiometry may be needed to achieve adequate ferromagnetic exchange coupling between the incorporated Co(2+) ions.
Related Concept Videos
01:06Nuclear Overhauser Enhancement (NOE)
03:02Colors and Magnetism
When atoms or molecules absorb light at the proper frequency, their electrons are excited to higher-energy orbitals. For many main group atoms and molecules, the absorbed photons are in the ultraviolet range of the electromagnetic spectrum, which cannot be detected by the human eye. For coordination compounds, the energy difference between the d orbitals often allows photons in the visible range to be absorbed and emitted, which is seen as colors by the human eye.