TiO2 nanorod arrays functionalized with In2S3 shell layer by a low-cost route for solar energy conversion

We report the fabrication and characterization of a TiO(2)-In(2)S(3) core-shell nanorod array structure for application of semiconductor-sensitized solar cells. Hydrothermally synthesized TiO(2) nanorod arrays on FTO glass substrates are functionalized with a uniform In(2)S(3) shell layer by using the successive ion layer adsorption and reaction (SILAR) method. This low-cost technique promotes a uniform deposition of In(2)S(3) nanoshells on the surface of TiO(2) nanorods, thus forming an intact interface between the In(2)S(3) shell and TiO(2) core. Results show that the thickness of In(2)S(3) shell layers as well as the visible light absorption threshold can be effectively controlled by varying the coating cycles during the SILAR process. The best reproducible performance of the sandwich solar cell using the TiO(2)-In(2)S(3) core-shell nanorod arrays as photoelectrodes was obtained after 30 SILAR cycles, exhibiting a short-circuit current (I(sc)) of 2.40 mA cm(-2), an open-circuit voltage (V(oc)) of 0.56 V, a fill factor (ff) of 0.40 and a conversion efficiency (η) of 0.54%, respectively. These results demonstrate a feasible and controllable route towards In(2)S(3) coating on a highly structured substrate and a proof of concept that such TiO(2)-In(2)S(3) core-shell architectures are novel and promising photoelectrodes in nanostructured solar cells.