Extreme superomniphobicity of multiwalled 8 nm TiO2 nanotubes

We report unprecedented superomniphobic characteristics of nanotube-structured TiO(2) surface fabricated by electrochemical etching and hydrothermal synthesis process, with the wettability contact angles for water and oil both being ∼174° or higher. A tangled forest of ∼8-nm-diameter, multiwalled nanotubes of TiO(2) was produced on the microtextured Ti surface, with the overall nanotube length controlled to 150 nm by adjusting the processing time. Wettability measurements indicate that the nanotube surface is extremely nonwettable to both water and oil. The contact angle of the 8 nm TiO(2) nanotube surface after perfluorosilane coating is extremely high (178°) for water droplets indicating superhydrophobic properties. The contact angle for oil, measured using a glycerol droplet, is also very high, about 174°, indicating superoleophobic characteristics. These dual nonwetting properties, superomniphobic characteristics, are in sharp contrast to the as-made TiO(2) nanotubes which exhibit superhydrophilic properties with a contact angle of essentially ∼0°. Such an extreme superomniphobic material made by a simple and versatile method can be useful for a variety of technical applications. It is interesting to note that all three properties can be obtained with identical nanotube structures. A nanometer-scaled structure introduced by hydrothermally grown TiO(2) nanotubes is an effective air trapping nanostructure in enhancing the amphiphobic (superomniphobic) wettability.