Effect of platinum on the photocatalytic degradation of chlorinated organic compound

TiO2 nanoparticles, doped with different Pt contents, were prepared by a modified photodeposition method using Degussa P-25 TiO2, H2PtCl6 6H2O and methanol as the solvents. The physicochemical properties of Pt/TiO2 were investigated by the nitrogen adsorption and desorption isotherm measurement technique, X-ray diffraction analysis and photoluminescence spectra, respectively. Reaction rates from photocatalytic removal of dichloromethane over Degussa P-25 TiO2 and Pt/TiO2 were evaluated. The average diameter and BET surface area of the TiO2 catalyst particles were 300 nm and 50 m2/g, respectively. The degradation efficiency was 99.0%, 82.7%, 55.2%, and 57.9% with TiO2 at inlet concentrations of 50, 100, 200, and 300 ppm, respectively. And the degradation efficiency was 99.3%, 79.7%, 76.5%, and 73.4% with a 0.005 wt.% Pt/TiO2 at inlet concentrations of 50, 100, 200, and 300 ppm, respectively. In addition, we found that the photoluminescence emission peak intensities decreased with increases in the doping amount of Pt, which indicates that the irradiative recombination was weakened. Furthermore, the results showed that the UV/0.005 wt.% Pt/TiO2 process was capable of efficiently decomposing gaseous DCM in air.