Rh-doped SrTiO3 photocatalyst electrode showing cathodic photocurrent for water splitting under visible-light
Katsuya Iwashina1, Akihiko Kudo
1Department of Applied Chemistry, Faculty of Science, Tokyo University of Science, 1-3 Kagurazaka, Shinjuku-ku, Tokyo 162-8601, Japan.
Abstract:
A Rh-doped SrTiO(3) (SrTiO(3):Rh) photocatalyst electrode that was readily prepared by pasting SrTiO(3):Rh powder onto a transparent indium tin oxide electrode gave a cathodic photocurrent under visible-light irradiation (λ > 420 nm), indicating that the SrTiO(3):Rh photocatalyst electrode possessed p-type semiconductor character. The cathodic photocurrent increased with an increase in the amount of doped Rh up to 7 atom %. The incident-photon-to-current efficiency at 420 nm was 0.18% under an applied potential of -0.7 V vs Ag/AgCl for the SrTiO(3):Rh(7 atom %) photocatalyst electrode. The photocurrent was confirmed to be due to water splitting by analyzing the evolved H(2) and O(2). The water splitting proceeded with the application of an external bias smaller than 1.23 V versus a Pt counter electrode under visible-light irradiation and also using a solar simulator, suggesting that solar energy conversion should be possible with the present photoelectrochemical water splitting.
More Related Videos
12:47Preparation and Use of Photocatalytically Active Segmented Ag|ZnO and Coaxial TiO2-Ag Nanowires Made by Templated Electrodeposition
Published on: May 2, 2014
10:21Developing Photosensitizer-Cobaloxime Hybrids for Solar-Driven H2 Production in Aqueous Aerobic Conditions
Published on: October 5, 2019