A novel structure for carbon nanotube reinforced alumina composites with improved mechanical properties

Engineering ceramics have high stiffness, excellent thermostability, and relatively low density, but their brittleness impedes their use as structural materials. Incorporating carbon nanotubes (CNTs) into a brittle ceramic might be expected to provide CNT/ceramic composites with both high toughness and high temperature stability. Until now, however, materials fabrication difficulties have limited research on CNT/ceramic composites. The mechanical failure of CNT/ceramic composites reported previously is primarily attributed to poor CNT-matrix connectivity and severe phase segregation. Here we show that a novel processing approach based on the precursor method can diminish the phase segregation of multi-walled carbon nanotubes (MWCNTs), and render MWCNT/alumina composites highly homogeneous. The MWCNTs used in this study are modified with an acid treatment. Combined with a mechanical interlock induced by the chemically modified MWCNTs, this approach leads to improved mechanical properties. Mechanical measurements reveal that only 0.9 vol% acid-treated MWCNT addition results in 27% and 25% simultaneous increases in bending strength (689.6 ± 29.1 MPa) and fracture toughness (5.90 ± 0.27 MPa m(1/2)), respectively.