Direct fabrication of all-cellulose nanocomposite from cellulose microfibers using ionic liquid-based nanowelding

All-cellulose nanocomposite was directly fabricated using nanowelding of cellulose microfibers as a starting material, in 1-butyl-3-methylimidazolium chloride (BMIMCl) as a solvent, for the first time. The average diameter of the reinforcing component (undissolved nanofibrils) in the nanocomposite made directly from cellulose microfibers (NC-microfiber) was 53 ± 16 nm. Owing to its high mechanical properties (tensile strength of 208 MPa and Young's modulus of 20 GPa), high transparency (76% at a wavelength of 800 nm), and complete barrier to air and biodegradability, the NC-microfiber is regarded as a high multiperformance material. The NC-microfiber made directly from cellulose microfibers showed similar macro-, micro-, and nanostructures and the same properties as those made from solvent-based welding of ground cellulose nanofibers (NC-nanofiber). Omitting the step of cellulose nanofiber production makes the direct production of all-cellulose nanocomposite from cellulose microfibers easier, shorter, and cheaper than using cellulose nanofibers as starting material. The direct nanowelding of macro/micrometer-sized materials is theorized to be a fundamental approach for making nanocomposites.