Preferred structures of the atomic Ag islands on silicone oil surfaces

Varying the substrate temperature T(s) from 285 to 353 K, both the aggregation behavior of Ag atoms and the preferred structures of the atomic Ag islands on silicone oil surfaces are investigated. After deposition, the deposited Ag atoms form isolated islands with a preferred height. Our observations reveal that, as T(s) increases, the preferred island height increases from 20.0 to 33.0 nm, which results in the decrease of the Ag apparent coverage, from 9.6 ± 0.1% to 6.5 ± 0.3%. Further, the crystal structure of the Ag islands changes from amorphous to polycrystalline as the substrate temperature T(s) goes up. Subsequently a 3D aggregation mechanism of the Ag atoms on the liquid substrates is proposed.