Separation of poly-3-hydroxyvalerate-co-3-hydroxybutyrate through gradient polymer elution chromatography

Polyhydroxyalkanoates are biodegradable polyesters produced by bacteria that can have a wide distribution in molecular weight, composition of monomers, and functionalities. This large distribution often leads to unpredictable physical properties making commercial applications challenging. To improve polymer homogeneity and obtain samples with a clear set of physical characteristics, poly-3-hydroxyvalerate-co-3-hydroxybutyrate copolymers were fractionated using gradient polymer elution chromatography (GPEC) as opposed to extensively used bulk fractionation. Separation was achieved using a reversed-phase column with chloroform and ethanol as the solvent and non-solvent, respectively. A separation was also conducted on a normal-phase column to compare elution patterns between columns of varied polarity. The fractions were analyzed using Size Exclusion Chromatography (SEC) and NMR to determine the percentage of 3-hydroxyvalerate in the copolymer as well as its molecular weight. It was found that as the percentage of "good" solvent was increased in the mobile phase, the polymers eluted with decreasing percentage of 3-hydroxyvalerate and increasing molecular weight which indicates the importance of precipitation/redissolution in the separation. The elution pattern of the polymer remained unchanged when using both a normal- and reversed-phase column which also illustrates the dominance of precipitation/redissolution in GPEC of polyhydroxyalkanoates. As such, GPEC is shown to be an excellent choice to provide polyhydroxyalkanoate samples with a narrower distribution in composition than the original bulk copolymer sample.