Enhanced electrical properties of textured NBBT ceramics derived from the screen printing technique
Mengjia Wu1, Youliang Wang, Dong Wang
1The Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, China.
Abstract:
(001)(pc)-oriented (Na(0.5)Bi(0.5))(0.94)Ba(0.06)TiO(3) (NBBT) lead-free piezoelectric ceramics were fabricated by the screen printing technique using Na(0.5)Bi(0.5)TiO(3) (NBT) templates. The plate-like NBT template particles were synthesized from bismuth layer-structured ferroelectric Bi(4)Ti(3)O(12) (BiT) precursors by the topochemical method. The screen printed NBBT ceramics with 20 wt% NBT templates contained a large fraction of grains aligned with their c-axis normal to the sample surface, giving a Lotgering factor of 0.486. The dielectric and ferroelectric properties of textured NBBT ceramics were anisotropic. Compared with the non-textured NBBT ceramics, the dielectric, ferroelectric, and piezoelectric properties of the textured NBBT ceramics were improved, giving a dielectric constant ϵ(T)(33)/ϵ(0) of 910, a remnant polarization P(r) of 29.2 μC/cm(2), a coercive field E(c) of 23.5 kV/cm, a piezoelectric coefficient d(33) of 180 pC/N, and a thickness-mode electromechanical coupling coefficient k(t) of 0.485.