Halogen lamp and LED activation of resin-modified glass ionomer restorative material. In vitro microhardness after
A Cassoni1, P Macarini, E S Leonetti
1Graduate Studies Division, Department of Restorative Dentistry, School of Dentistry, Guarulhos University, Brazil. acassoni@prof.ung.br
Aim:
The purpose of this study was to evaluate the activation of resin-modified glass ionomer restorative material (RMGI, Vitremer-3M-ESPE, A3) by halogen lamp (QTH) or light-emitting diode (LED) by Knoop microhardness (KHN) in two storage conditions: 24 hrs and 6 months and in two depths (0 and 2 mm).
Materials And Methods:
The specimens were randomly divided into 3 experimental groups (n = 10) according to activation form and evaluated in depth after 24 h and after 6 months of storage. Activation was performed with QTH for 40s (700 mW/cm) and for 40 or 20 s with LED (1,200 mW/cm2). After 24 hrs and 6 months of storage at 37 degrees C in relative humidity in light-proof container, the Knoop microhardness test was performed. Statistics Data were analysed by three-way ANOVA and Tukey post-tests (p < 0.05).
Results:
All evaluated factors showed significant differences (p < 0.05). After 24 hrs there were no differences within the experimental groups. KHN at 0 mm was significantly higher than 2 mm. After 6 months, there was an increase of microhardness values for all groups, being the ones activated by LED higher than the ones activated by QTH.
Conclusion:
Light-activation with LED positively influenced the KHN for RMGI evaluated after 6 months.