Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

Fracture susceptibility of worn teeth

Amanda J Keown1, Mark B Bush, Chris Ford

  • 1School of Mechanical and Chemical Engineering, University of Western Australia, Crawley WA 6009, Australia.

Journal of the Mechanical Behavior of Biomedical Materials
|November 22, 2011
PubMed

Keywords:
dental wear simulationtooth fracture resistancebiomechanical modelingevolutionary dental adaptation

More Related Videos

Fracture Apparatus Design and Protocol Optimization for Closed-stabilized Fractures in Rodents06:59

Fracture Apparatus Design and Protocol Optimization for Closed-stabilized Fractures in Rodents

Published on: August 14, 2018

Practical Considerations for the Design, Execution, and Interpretation of Studies Involving Whole-Bone Bending Tests of Rodent Bones04:20

Practical Considerations for the Design, Execution, and Interpretation of Studies Involving Whole-Bone Bending Tests of Rodent Bones

Published on: September 1, 2023

Related Concept Videos

Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
Fractures: Bone Repair01:27

Fractures: Bone Repair

Treatment for a fracture is based on the type of break, the bone affected, and the patient's age.
Minor fractures with no bone displacement are treated by immobilizing the fractured bone using a cast or splint. However, in the case of fractures with displaced bones, the broken bones are repositioned before immobilization to ensure successful healing without deformation and loss of function. The realignment of fractured bone ends is performed through a process called reduction. If the procedure...