Hydrogen reactivity on highly-hydroxylated TiO2(110) surfaces prepared via carboxylic acid adsorption and photolysis

Combined scanning tunneling microscopy, temperature programmed desorption, photo stimulated desorption, and density functional theory studies have probed the formation and reactivity of highly-hydroxylated rutile TiO(2)(110) surfaces, which were prepared via a novel, photochemical route using trimethyl acetic acid (TMAA) dissociative adsorption and subsequent photolysis at 300 K. Deprotonation of TMAA molecules upon adsorption produces both surface bridging hydroxyls (OH(b)) and bidentate trimethyl acetate (TMA) species with a saturation coverage of nearly 0.5 monolayers (ML). Ultra-violet light irradiation selectively removes TMA species, producing a highly-hydroxylated surface with up to ~0.5 ML OH(b) coverage. At high coverages, the OH(b) species typically occupy second-nearest neighbor sites along the bridging oxygen row locally forming linear (2 × 1) structures of different lengths, although the surface is less ordered on a long scale. The annealing of the highly-hydroxylated surface leads to hydroxyl recombination and H(2)O desorption with ~100% yield, thus ruling out the diffusion of H into the bulk that has been suggested in the literature. In agreement with experimental data, theoretical results show that the recombinative H(2)O desorption is preferred over both H bulk diffusion and H(2) desorption processes.