Thermal stability of Mg/Co multilayer with B4C, Mo or Zr diffusion barrier layers
Jingtao Zhu1, Sika Zhou, Haochuan Li
1Department Institute of Precision Optical Engineering, Department of Physics, Tongji University, Shanghai 200092, China.
Abstract:
The efficiency of B(4)C, Mo and Zr barrier layers to improve thermal stability of Mg/Co multilayer up to 400 °C is investigated. Multilayers were deposited by direct current magnetron sputtering and characterized using X-ray and extreme ultraviolet reflection. The results suggest that B(4)C barrier layer is not effective due to drastic diffusion at Mg-B(4)C interface. Although introducing Mo barriers improves the thermal stability from 200 to 300 °C, it increases the interface roughness and thus degrades the optical performances. On the contrary, Zr barriers can significantly increase the thermal stability of Mg/Co up to 400 °C without optical performance degradation. Thus, Mg/Zr/Co/Zr is suitable for EUV applications requiring both optimal optical performances and heat resistance.