Preparation and characterization of thermoplastic materials for invisible orthodontics

PETG/PC/TPU polymer blend was prepared by mechanical blending. The mechanical properties of modified PETG/PC/TPU blend were characterized using a universal testing machine, and results were compared against two commercial thermoplastic products -Erkodur and Biolon. Blending modification improved the properties of PETG/PC/TPU. When blending ratio (wt%) was 70/10/20, PETG/PC/TPU exhibited optimal mechanical properties which exceeded those of Erkodur and Biolon. Tear strength was 50.23 MPa and elongation at break was 155.99%. Stress relaxation rate was 0.0136 N/s after 1 hour, which was significantly slower than Erkodur and Biolon (p<0.05). Water absorption rate was 0.57% after 2 weeks, which was significantly lower than Erkodur and Biolon (p<0.05).