Calcium phosphate-hybridized tendon graft to enhance tendon-bone healing two years after ACL reconstruction in goats
Hirotaka Mutsuzaki1, Masataka Sakane
1Department of Orthopaedic Surgery, Institute of Clinical Medicine, Graduate School of Comprehensive Human Sciences, University of Tsukuba, 1-1-1 Tennodai, Tsukuba, Ibaraki 305-8575, Japan. sakane-m@md.tsukuba.ac.jp.
Background:
We developed a novel technique to improve tendon-bone attachment by hybridizing calcium phosphate (CaP) with a tendon graft using an alternate soaking process. However, the long-term result with regard to the interface between the tendon graft and the bone is unclear.
Methods:
We analyzed bone tunnel enlargement by computed tomography and histological observation of the interface and the tendon graft with and without the CaP hybridization 2 years after anterior cruciate ligament (ACL) reconstruction in goats using EndoButton and the postscrew technique (CaP, n = 4; control, n = 4).
Results:
The tibial bone tunnel enlargement rates in the CaP group were lower than those in the control group (p < 0.05). In the CaP group, in the femoral and tibial bone tunnels at the anterior and posterior of the joint aperture site, direct insertion-like formation that contained a cartilage layer without tidemarks was more observed at the tendon-bone interface than in the control group (p < 0.05). Moreover, the gap area between the tendon graft and the bone was more observed at the femoral bone tunnel of the joint aperture site in the control group than in the CaP group (p < 0.05). The maturation of the tendon grafts determined using the ligament tissue maturation index was similar in both groups.
Conclusions:
The CaP-hybridized tendon graft enhanced the tendon-bone healing 2 years after ACL reconstruction in goats. The use of CaP-hybridized tendon grafts can reduce the bone tunnel enlargement and gap area associated with the direct insertion-like formation in the interface near the joint.