Effect of aging on the morphology of bitumen by atomic force microscopy

Effect of aging on the morphology of bitumen was investigated. Two bitumens were aged according to the thin film oven test (TFOT), pressure aging vessel (PAV) test and ultraviolet (UV) radiation, respectively. The morphology of the binders before and after aging was characterized by atomic force microscopy. The physical properties and chemical compositions of the binders were also measured. The results showed that aging affected the bitumen morphology significantly. Aging increased the overall surface stiffness of the bitumen and made the bitumen surface more solid-like. The extent of these changes was dependent on aging conditions. TFOT decreased the contrast between the dispersed domains and the matrix, which contributed to the single-phase trend of the binders. The effect of PAV aging on morphology of the binders was dependent on the base bitumen. In one case, it further accelerated the single-phase trend of bitumen in comparison with that after TFOT. In the other case, it caused the phase separation of bitumen. In both cases, PAV aging increased the surface roughness of the binders obviously. As a result of UV aging, the contrast between the matrix phase and dispersed phase was increased due to the difference in sensitivity to UV radiation of the bitumen molecules, which caused or further promoted the phase separation in the binders. Regardless of the aging procedure carried out, a strong correlation was observed between the changes in morphology and physical properties as well as chemical compositions of the binders before and after aging.