The effect of pH on the degradation of biodegradable poly(L-lactide-co-glycolide) 80/20 urethral stent material in
Hanne Juuti1, Andres Kotsar, Joonas Mikkonen
1Department of Biomedical Engineering, Tampere University of Technology, Tampere, Finland.
Purpose:
To investigate in vitro whether pH ranging between 6 and 9 has an effect on the degradation of stent fibers made of poly(l-lactide-co-glycolide) (PLGA) 80/20.
Materials And Methods:
The fibers were divided into three groups and immersed in sodium phosphate-buffered saline (Na-PBS) solution with three different pH values: 6, 7.4, and 9. The mechanical and thermal properties were studied, and scanning electron microscopy (SEM) images were taken at specific time points of hydrolysis.
Results:
The tensile testing showed that the strength of the fibers decreased through hydrolysis and was lost at 8 weeks in all groups. The T(m) and T(g) of the PLGA fibers did not indicate any significant differences between the different groups. In SEM images taken at 4 weeks, there were no significant differences between the fibers immersed in Na-PBS solutions of different pH values. However, at 8 weeks the surface of the fiber immersed in saline with a pH of 6 seemed coarser than that of those immersed in neutral (pH 7.4) or alkaline (pH 9) Na-PBS.
Conclusion:
The studied pH values did not influence the degradation behavior of the PLGA 80/20 fibers. Therefore, rabbits can be used as model animals for human biodegradable urological devices even though the pH of their urine is different.