Effectiveness of self-adhesive luting cements in bonding to chlorhexidine-treated dentin
Vinicius Di Hipólito1, Flávia Pires Rodrigues, Fabiana Bárbara Piveta
1Biomaterials Research Group, Anhanguera - Bandeirante University of São Paulo - UNIBAN, School of Dentistry, Brazil. vdhipolito@yahoo.com.br
Objectives:
The aim was to investigate the microtensile bond strength (μ-TBS) and failure pattern of self-adhesive luting cements (SLC) to dentin pre-treated with different concentrations of chlorhexidine (CHX) solutions.
Methods:
The occlusal enamel was removed from 30 extracted sound human molars in order to expose a flat dentin. Resin-composite (Filtek Z250, 3M ESPE) discs (12 mm in diameter, 6.0mm thickness) were cemented to the smear layer-covered dentin using the SLC [RelyX U100, 3M ESPE (U100); Multilink Sprint, Ivoclar Vivadent (MS)] with 0.2% or 2.0% CHX solutions. Results were compared with the control, untreated dentin. Six groups were then created based on the SLC and dentin pre-treatment (n=5). After 24h of water storage, restored teeth were serially sectioned into beams with a cross-sectional area of 0.8mm(2) at the bonded interface. Subsequently, specimens were tested in tension with a crosshead speed of 0.5mm/min in a universal testing machine, and the failure patterns were classified. Two-way ANOVA and Tukey's tests were performed (α=0.05). Additionally, 18 teeth were subjected to energy-dispersive X-ray spectroscopy (EDS) analysis and micromorphology characterization of the smear layer-covered dentin and 0.2% or 2.0% CHX-treated dentin surfaces.
Results:
The μ-TBS obtained for both control groups were significantly higher, regardless of the CHX concentration and/or the cement used. Bond strengths were significantly higher for U100 than for MS, except when 2.0% CHX was applied. Fractographic analysis indicated that most failures in the control groups occurred cohesively in the SLC. Pre-treated dentin with 0.2% and 2.0% CHX solutions presented higher incidences of adhesive failures. EDS/SEM analysis exhibited varied concentrations of chlorine ions and crystal-shaped precipitates, depending upon the CHX concentration.
Significance:
Pre-treatment of dentin with 0.2% or 2.0% CHX adversely affects the bonding efficacy when associated with the SLCs tested.