Controlled fabrication of flower-like nickel oxide hierarchical structures and their application in water treatment

Flower-like NiO hierarchical structures with 2-5 μm diameter assembled from nanosheet building blocks have been successfully fabricated via a wet-chemical method combined with thermodecomposition technology. The template-free method is facile and effective in preparing flower-like NiO superstructures in high yield. The intermediate product and final hierarchical structures are characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform IR (FTIR), and thermogravimetric analysis (TGA). The effects of growth temperature and reaction time on the morphologies of the as-prepared structures were investigated by SEM characterization and a possible mechanism for the formation of flower-like NiO is proposed. Based on the nitrogen adsorption and desorption measurements, the BET surface area of the as-obtained sample is 55.7 m²/g and the pore-size distribution plot indicates a bimodal mesopore distribution, with pore sizes of ca. 2.6 nm and 7.4 nm, respectively. In comparison with sphere-like and rod-like structures, the flower-like NiO hierarchical structures show an excellent ability to rapidly remove various pollutants when used as adsorbent and photocatalyst in waste-water treatment, which may be attributed to its unique hierarchical and porous surface structures.