Growth, mechanical, thermal and spectral properties of Cr3+:MgMoO4 crystal

This paper reports the growth, mechanical, thermal and spectral properties of Cr(3+):MgMoO(4) crystals. The Cr(3+):MgMoO(4) crystals with dimensions up to 30 mm×18 mm×14 mm were obtained by TSSG method. The absorption cross-sections of (4)A(2)→(4)T(1) and (4)A(2)→(4)T(2) transitions are 12.94×10(-20) cm(2) at 493 nm and 7.89×10(-20) cm(2) at 705 nm for E//N(g), respectively. The Cr(3+):MgMoO(4) crystal shows broad band emission extending from 750 nm to 1300 nm with peak at about 705 nm. The emission cross-section with FWHM of 188 nm is 119.88×10(-20) cm(2) at 963 nm for E//N(g). The investigated results showed that the Cr(3+):MgMoO(4) crystal may be regarded as a potential tunable laser gain medium.