Microleakage of IPS empress 2 inlay restorations luted with self-adhesive resin cements

To assess the microleakage of three self-adhesive and one etch-and-rinse resin cements when luting IPS Empress 2 (Ivoclar Vivadent, Liechtenstein) all-ceramic inlay restorations to the prepared cavities in extracted human molars.

The cylindrical Class V cavities were prepared on the buccal surfaces of 40 extracted human third molars using diamond burs. The IPS Empress 2 ceramic inlays were placed with Multilink Sprint (Ivoclar Vivadent), RelyX Unicem (3M ESPE, USA), G-Cem (GC, Japan), or Variolink II (Ivoclar Vivadent) as the control group. After storage in distilled water at 37°C for 24 hours, samples were subjected to 1000 thermal cycles between baths of 5°C and 55°C, with a dwell time of 30 seconds. The microleakage scores were examined on the occlusal and gingival margins at 30× magnification after each sample was stained with 0.5% basic fuchsin and sectioned into three parts using a thin diamond blade (Isomet, Buehler, USA) (n=40). The extent of microleakage on both occlusal and gingival margins of the restorations was scored and recorded. The microleakage data were analyzed using Kruskall-Wallis and Mann-Whitney U-tests.

Statistically significant differences were observed between the groups in both margins according to the Kruskall-Wallis and Mann-Whitney U-tests (p<0.05). Microleakage scores on the occlusal margins were Variolink II < RelyX Unicem < G-Cem = Multilink Sprint. Microleakage scores on the gingival margins are Variolink II = RelyX Unicem < G-Cem < Multilink Sprint.

Self-adhesive resin cements displayed higher microleakage scores on the occlusal margins, whereas on the gingival margins RelyX Unicem showed comparable microleakage results with the control samples.