Hierarchical nitrogen doped bismuth niobate architectures: controllable synthesis and excellent photocatalytic...

Nitrogen doped bismuth niobate (N-Bi(3)NbO(7)) hierarchical architectures were synthesized via a facile two-step hydrothermal process. XRD patterns revealed that the defect fluorite-type crystal structure of Bi(3)NbO(7) remained intact upon nitrogen doping. Electron microscopy showed the N-Bi(3)NbO(7) architecture has a unique peony-like spherical superstructure composed of numerous nanosheets. UV-vis spectra indicated that nitrogen doping in the compound results in a red-shift of the absorption edge from 450nm to 470nm. XPS indicated that [Bi/Nb]N bonds were formed by inducing nitrogen to replace a small amount of oxygen in Bi(3)NbO(7-x)N(x), which is explained by electronic structure calculations including energy band and density of states. Based on observations of architectures formation, a possible growth mechanism was proposed to explain the transformation of polyhedral-like nanoparticles to peony-like microflowers via an Ostwald riping mechanism followed by self-assembly. The N-Bi(3)NbO(7) architectures due to the large specific surface area and nitrogen doping exhibited higher photocatalytic activities in the decomposition of organic pollutant under visible-light irradiation than Bi(3)NbO(7) nanoparticles. Furthermore, an enhanced photocatalytic performance was also observed for Ag/N-Bi(3)NbO(7) architectures, which can be attributed to the synergetic effects between noble metal and semiconductor component.