Hollow silica capsules with well-defined asymmetric windows in the shell

A straightforward and effective approach to fabricate porous silica capsules with well-defined asymmetric windows in the shell using raspberry-like templates has been developed. This process begins with the formation of a hierarchical template by chemically coupling a large polystyrene sphere to an ensemble of small, polystyrene latex spheres. The hierarchical template in conjunction with a hard templating method and spin-coating leads to silica capsules with well-defined, asymmetric pores (windows) in the outer shell. Proof-of-principle of this approach has been demonstrated using a 1500/110 nm hierarchical template. The silica capsules thus produced were characterized with scanning electron microscopy and STEM. The diameter of the capsules was ~1400 nm, and the outer opening of the windows was ~100 nm in size, consistent with the diameters of the core and satellite spheres considering the shrinkage due to the calcination. The inner opening was ~30 nm, which gives rise to an asymmetry factor, defined as the diameter of the outer window to the diameter of the inner window, of ~3. In another example, surface-bound capsules with an asymmetry factor of ~1 were made. Collectively, these windows can provide efficient pathways to connect the inside of the capsule to the outside and have potential for asymmetric diffusion and rectification.