Preparation of biocompatible chitosan grafted poly(lactic acid) nanoparticles

Chitosan grafted poly(lactic acid) (CS-g-PLA) copolymer was synthesized and characterized by FT-IR and elemental analysis. The degree of poly(lactic acid) substitution on chitosan was 1.90 ± 0.04%. The critical aggregation concentration of CS-g-PLA in distilled water was 0.17 mg/ml. Three methods of preparing CS-g-PLA nanoparticles (diafiltration method, ultrasonication method and diafiltration combined with ultrasonication method) were investigated and their effect was compared. Of the three methods, diafiltration combined with ultrasonication method produced nanoparticles with optimal property in terms of size and morphology, with size ranging from 133 to 352 nm and zeta potential from 36 to 43 mV. Also, the hemolytic activity and cytotoxicity of the CS-g-PLA based nanoparticles was tested, and results showed low hemolysis rate (<5%) and no significant cytotoxicity effect of these nanoparticles.