Evaluation of the Curing of Adhesive Systems by Rheological and Thermal Testing
09:06

Evaluation of the Curing of Adhesive Systems by Rheological and Thermal Testing

Published on: July 3, 2020

Interplay between viscoelastic and chemical tunings in fatty-acid-based polyester adhesives: engineering biomass

Richard Vendamme1, Katrien Olaerts, Monica Gomes

  • 1Nitto Denko Corporation's European Research Committee (ERC), Nitto Europe NV, Genk, Belgium. richard_vendamme@nittoeur.com

Biomacromolecules
|May 23, 2012
PubMed

More Related Videos

Microwave-assisted Functionalization of Poly(ethylene glycol) and On-resin Peptides for Use in Chain Polymerizations and Hydrogel Formation15:33

Microwave-assisted Functionalization of Poly(ethylene glycol) and On-resin Peptides for Use in Chain Polymerizations and Hydrogel Formation

Published on: October 29, 2013

Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing09:39

Characterizing Dissipative Elastic Metamaterials Produced by Additive Manufacturing

Published on: June 28, 2024

Related Concept Videos

Types of Step-Growth Polymers: Polyesters01:20

Types of Step-Growth Polymers: Polyesters

The introduction of polyesters has brought major development to the textile industry. The wrinkle-free behavior of polyester blends has eliminated the need for starching and ironing clothes.
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the polymer...
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
Classification and Mechanical Properties of Synthetic Polymers01:28

Classification and Mechanical Properties of Synthetic Polymers

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)00:53

Olefin Metathesis Polymerization: Acyclic Diene Metathesis (ADMET)

Acyclic diene metathesis polymerization or ADMET polymerization involves cross-metathesis of terminal dienes, such as 1,8-nonadiene, to give linear unsaturated polymer and ethylene. As ADMET is a reversible process, the formed ethylene gas must be removed from the reaction mixture to complete the polymerization process.
Similar to cross-metathesis, ADMET also involves the formation of metallacyclobutane intermediate by [2+2] cycloaddition of one of the double bonds of a terminal diene with...
Anionic Chain-Growth Polymerization: Overview01:20

Anionic Chain-Growth Polymerization: Overview

The polymerization process that involves carbanion as an intermediate is called anionic polymerization. It is also a type of addition or chain-growth polymerization. Anionic polymerization gets initiated by a strong nucleophile such as an organolithium or a Grignard reagent. The most commonly used initiator for anionic polymerization is butyl lithium. Monomers involved in anionic polymerization must possess a vinyl group bonded to one or two electron-withdrawing groups. For instance,...