Density and birefringence of a highly stable α,α,β-trisnaphthylbenzene glass

Spectroscopic ellipsometry has been used to understand the properties of α,α,β-trisnaphthylbenzene (ααβ-TNB) glasses vapor-deposited at a substrate temperature of 295 K (0.85 T(g)). In a single temperature ramping experiment, a range of properties of the as-deposited glass can be measured, including density, fictive temperature, onset temperature, thermal expansion coefficient, and birefringence. The vapor-deposited ααβ-TNB glass is 1.3% more dense than the ordinary glass prepared by cooling at 1 K/min, is found to be birefringent, has a fictive temperature 35 K below that of the ordinary glass, and an onset temperature 20 K above that of the ordinary glass. The thermal expansion coefficient of the vapor-deposited ααβ-TNB glass is 14% lower than that of the ordinary glass, indicating that lower portions of the potential energy landscape have more harmonic potential minima than the parts accessible to the ordinary glass.