Leaching of metal(loid)s from a construction material: influence of the particle size, specific surface area and...

Construction materials are tested worldwide for a potential release of dangerous substances to prevent adverse effects on humans and biota. It is crucial to identify and understand the processes which are decisive for the release of hazardous substances. The current study compares the results of different test methods. Taking copper slag as model material, the influence of material particle size, eluant composition and ionic strength was tested. Ionic strength and salinity significantly influenced the release of metal(loid)s in the water phase. Furthermore, it was elucidated that colloids can cause methodological artefacts. The available specific surface area exhibited a positive correlation with the release of hazardous substances. The specific surface areas of materials were determined by the Brunauer, Emmett and Teller model (BET) and four other methods. The aluminium foil method showed the best results with regard to the statistical uncertainty, compared to a 3D laser scanning method. With help of the roughness factor λ it is possible to compare the results from surface area measurements with different material particle sizes (0-250 mm). This comparability offers the potential to match the release of metal(loid)s from laboratory studies with field applications and catchment area calculations/modelling, based on the release per m(2).