One-step synthesis of biodegradable curcumin-derived hydrogels as potential soft tissue fillers after breast cancer
Nava Shpaisman1, Larisa Sheihet, Jared Bushman
1New Jersey Center for Biomaterials and Department of Chemistry and Chemical Biology, Rutgers, The State University of New Jersey, Piscataway, New Jersey 08854, United States.
Abstract:
A one-step synthesis of a curcumin-derived hydrogel (curcumin content of 25-75 mol %) is reported. Curcumin is incorporated into the hydrogel backbone and cross-linked through biodegradable carbonate linkages. Curcumin as a part of the polymer backbone is protected from oxidation and degradation, while hydrogel hydrolysis results in the release of active curcumin. Nontoxic poly(ethylene glycol) and desaminotyrosyl-tyrosine ethyl ester are used to tune the hydrophilic/hydrophobic hydrogel properties. In this way, hydrogels with a wide range of physical properties including water-uptake (100-550%) and compression moduli (7-100 kPa) were obtained. Curcumin release is swelling-controlled and could be extended to 80 days. In vitro, curcumin-derived hydrogels showed selective cytotoxicity against MDA-MB-231 (IC(50) 9 μM) breast cancer cells but no cytotoxicity to noncancerous quiescent human dermal fibroblasts even at high curcumin concentrations (160 μM). One possible application of these curcumin-derived hydrogels is as soft tissue filler after surgical removal of cancerous tissue.