Application of hydrogel polymers for development of thyrotropin releasing hormone-loaded adhesive buccal patches

To utilize hydrogels for fabricating thyrotropin releasing hormone (TRH) adhesive buccal patches, type of hydrogels such as polyacrylic acids (Polycarbophil AA1, Carbopols 934P, 974P and 971P), celluloses (HPMC K4M, K4MCR and K15M), polysaccharide (sodium alginate) and polyacrylic acid combinations with either cellulose or polysaccharide were evaluated for adhesion force, water uptake and swelling capacity. Upon the characterization of hydrogel polymers, TRH-loading of patches fabricated from these hydrogels was evaluated at various polymer concentrations, combinations and ratios and then in vitro release kinetics of TRH from these patches were studied. Results indicated that maximum adhesion force was shown by polyacrylic acids. Adhesive force of polymer combination mainly resulted from combination of adhesive force, according to ratio proportion used, of each polymer without any superimposed effect of polymer combination. Polycarbophil AA1 showed highest water uptake and swelling capacity. Maximum TRH-loading was obtained with sodium alginate and Polycarbophil AA1 and sodium alginate combination. TRH release profiles revealed that release was sustained from Polycarbophil AA1 and its combination with celluloses or polysaccharide at 2:1 level of polymer ratio. Based on adhesion, loading and release characteristics, patches of Polycarbophil AA1 with K4M, K4MCR and sodium alginate were concluded to be suitable for further development.