Preparation of Nafion-Ru(bpy)3(2+)-chitosan/gold nanoparticles composite film and its electrochemiluminescence...

In this research, it was found that a composite film could be formed by mixing Nafion with chitosan on the graphite electrode surface. Then, based on the strong absorption of both chitosan for AuCl(4)(-) and Nafion for Ru(bpy)(3)(2+), respectively, the gold nanoparticles and electrochemiluminescence (ECL) active molecules, Ru(bpy)(3)(2+), were effectively incorporated into the composite film of chitosan with Nafion. Lastly, based on the interaction of Ru(bpy)(3)(2+) with Nafion inside the Nafion-chitosan/gold nanoparticles film, Ru(bpy)(3)(2+) was successfully immobilized within this composite film. In this case, a new composite film for fabricating Ru(bpy)(3)(2+)-based ECL sensors was developed. The performances of this composite film were characterized by transmission electron microscopy (TEM), electrochemistry and electrochemiluminescence methods. Our results showed that: firstly, the gold nanoparticles in the resulting composite film could act as conducting pathways to connect Ru(bpy)(3)(2+) sites; the electrode surface accelerated the charge transport through the composite film, and the diffusion coefficient of Ru(bpy)(3)(2+) within this composite film modified electrode was 65 times higher than that of the pure Nafion film modified electrode. Secondly, due to its unique polymeric cationic character and better film-forming properties, chitosan could improve the compact structure of pure Nafion and greatly enhance the mass-transfer speed of Ru(bpy)(3)(2+). Then, the co-reactant tripropylamine (TPA) inside the composite film could offer better ECL performances such as more rapid ECL response speed, longer-term stability and higher sensitivity compared with the performances of pure Nafion film.