The elastic moduli of human subchondral, trabecular, and cortical bone tissue and the size-dependency of cortical...

The elastic moduli of human subchondral, trabecular, and cortical bone tissue from a proximal tibia were experimentally determined using three-point bending tests on a microstructural level. The mean modulus of subchondral specimens was 1.15 GPa, and those of trabecular and cortical specimens was 4.59 GPa and 5.44 GPa respectively. Significant differences were found in the modulus values between bone tissues, which may have mainly resulted from the differences in the microstructures of each bone tissue rather than in the mineral density. Furthermore, the size-dependency of the modulus was examined using eight different sizes of cortical specimens (heights h = 100-1000 microns). While the modulus values for relatively large specimens (h greater than 500 microns) remained fairly constant (approximately 15 GPa), the values decreased as the specimens became smaller. A significant correlation was found between the modulus and specimen size. The surface area to volume ratio proved to be a key variable to explain the size-dependency.