Kinetics of polymerization and contraction stress development in self-adhesive resin cements

A Frassetto1, C O Navarra, G Marchesi

  • 1Department of Medical Sciences, University of Trieste, Italy.

Dental Materials : Official Publication of the Academy of Dental Materials
|July 10, 2012
PubMed
Abstract

More Related Videos

Stereolithographic 3D Printing with Renewable Acrylates08:28

Stereolithographic 3D Printing with Renewable Acrylates

Published on: September 12, 2018

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

Related Concept Videos

Actin Polymerization01:42

Actin Polymerization

Actin polymerization occurs through the head-to-tail association of binding sites on monomeric actin or G-actin to form filamentous or F-actin. The polymerization can be divided into three phases ̶  nucleation, elongation, and steady-state phase.
The nucleation phase involves forming a stable nucleus consisting of three actin monomers to form a new actin filament. Actin-binding proteins such as formins and Arp2/3 complex help filament growth post-nucleation. The Formins form straight actin...
Cationic Chain-Growth Polymerization: Mechanism00:57

Cationic Chain-Growth Polymerization: Mechanism

The cationic polymerization mechanism consists of three steps: initiation, propagation, and termination. In the initiation step of the polymerization process, the π bond of a monomer gets protonated by the Lewis acid catalyst, which is formed from boron trifluoride and water. The protonation of the π bond generates a carbocation stabilized by the electron‐donating group. In the propagation step, the π bond of the second monomer acts as a nucleophile and attacks the generated carbocation,...
Creep in Concrete01:22

Creep in Concrete

Creep refers to the time-dependent increase in strain under a sustained load, excluding other time-dependent deformations associated with shrinkage, swelling, and thermal expansion in concrete. The primary mechanism behind creep involves the loss of physically adsorbed water from the calcium silicate hydrate within the hydrated cement paste. This process is further exacerbated by concrete's non-linear stress-strain relationship, microcrack development in the interfacial transition zone, and...
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in ASTM C...
Plastic Behavior01:21

Plastic Behavior

A material's elastic behavior is characterized by the disappearance of stress once the load is removed, allowing the material to return to its original state. However, when stress surpasses the yield point, yielding commences, marking the onset of plastic deformation or permanent set. This change from elastic to plastic behavior is influenced by the peak stress value and the duration before the load is removed. An intriguing observation occurs when a specimen is loaded, unloaded, and reloaded.
Accelerated Curing of Concrete01:25

Accelerated Curing of Concrete

Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...