Morphology Control for Fully Printable Organic–Inorganic Bulk-heterojunction Solar Cells Based on a Ti-alkoxide and Semiconducting Polymer
Published on: January 10, 2017
Preparation and characterization of high molecular weight low bandgap polymers based on poly(2,7-carbazole)s for
Eun Young Park1, Jaewook Jung, So Youn Nam
1Advanced Materials Division, Korea Research Institute of Chemical Technology (KRICT), Deajeon 305-600, South Korea.
Abstract:
We report the PCDTBT {Poly[N-9'-heptadecanyl-2,7-carbazole-alt-5,5-(4',7'-di-2-thienyl-2',1',3'-benzothiadiazole)]}, an alternating copolymer of 2,7-carbazole and dithienyl-2,1,3-benzothiazole, has high molecular weight and narrow molecular weight distribution. Our PCDTBT can be successfully prepared as good yield by using tetrakis(triphenylphosphine)palladium [Pd(PPh3)4] catalyst instead of Pd2dba3/P(o-Tol)3 catalyst. From the UV/Vis absorption spectroscopy, we can observe that absorption bands of PCDTBT are bathochromically shifted by increasing the molecular weight, that is to say, our high molecular weight PCDTBT can absorb much longer wavelength light compare to low molecular weight PCDTBT. The best performance can be obtained from device based on the mixture of PCDTBT (polymer-30) and PC70BM {[6,6]-phenyl C71-butyric acid methyl ester} (1:4) as an active layer, which shows 4.50% of PCE with 10.1 mA/cm2 of short-circuit current density (J(SC)), 0.85 V of open-circuit voltage (V(OC)), and 52.3% of fill factor which is very similar with Leclerc's published result.