Compositional characterization of GaAs/GaAsSb nanowires by quantitative HAADF-STEM

The Sb concentration in axial GaAs(1-x)Sb(x) inserts of otherwise pure GaAs nanowires has been investigated with quantitative high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). The Sb concentration was quantified by comparing the experimental image intensities normalized to the incident beam intensity with intensities simulated with a frozen lattice multislice approach. Including static atomic displacements in the simulations was found to be crucial for correct compositional analysis of GaAs(1-x)Sb(x). HAADF intensities of individual nanowires were analysed both across the nanowires, exploiting their hexagonal cross-sectional shape, and along the evenly thick central part of the nanowires. From the cross-sectional intensity profiles, a decrease in the Sb concentration towards the nanowire outer surfaces was found. The longitudinal intensity profiles revealed a gradual build-up of Sb in the insert. The decrease of the Sb concentration towards the upper interface was either gradual or abrupt, depending on the growth routine chosen. The compositional analysis with quantitative HAADF-STEM was verified by energy dispersive X-ray spectroscopy.