Size and oxygen passivation induced reversal of photoconducting behaviour in CdS nanorods

The effect of oxygen adsorption and desorption on the photoconducting gain, spectral dependence of quantum efficiency and optical switching was studied in CdS nanorods with diameters of 20, 50 and 100 nm. These were found to have an increasing degree of crystallinity and consequently a decreasing overall density of defects leading to better stoichiometry being maintained. These properties, along with the complete depletion of electrons from the nanorod volume and oxygen induced passivation of defects, resulted in: (i) a large difference in photoconducting gain, (ii) reversal of the photoconducting behaviour on annealing in oxygen and a vacuum, and (iii) onset of an absorption edge in the spectral dependence of quantum efficiency on oxygen annealing in 20 nm diameter nanorods in comparison to the normal photoconducting behaviour expected from an n-type semiconductor observed in 50 and 100 nm diameter nanorods. Single CdS nanorod devices show stable I-V characteristics in dark and light conditions under a wide temperature range and the effect of oxygen and vacuum annealing can be clearly observed. The oxygen induced defect passivation observed in this study is important for the application of compound semiconductor nanorods in optoelectronic devices.