Histological ex vivo analysis of retrieved human tantalum augmentations
Stefan Breer1, Michael Hahn, Daniel Kendoff
1Department of Osteology and Biomechanics, University Medical Center Hamburg-Eppendorf, Lottestraße 59, 22529 Hamburg, Germany.
Purpose:
The characteristics of tantalum augment osseointegration in human ex vivo specimens from re-revision procedures are unknown and limited data in this regard is available. The purpose of this study was to investigate the osseointegration pattern into porous tantalum augmentations harvested during re-revision procedures.
Methods:
Between 2007 and 2010 a total of 324 hip and knee revisions with a tantalum augmentation were performed in our institution. Out of this cohort, seven patients (2.2 %) had to be re-revised. To analyse the status of trabecular ingrowth in the retrieved cases (four hips, three knees), all specimens were analysed by contact radiography, subjected to undecalcified processing, histology, thin-section analysis and backscattered electron imaging.
Results:
Trabecular and vascular ingrowth could be found along the bone-augment-interface in two of seven revised specimens, respectively. The depth of bone ingrowth reached up to 2.6 mm. However, the analysis of the remaining cases revealed no bony ingrowth into trabecular metal. Rather, large parts of the implants were embedded in cement or pores were filled with autologous bone.
Conclusions:
Although the cause for the missing bony ingrowth seems to be multifactorial, some fundamental conditions, such as the provision of the greatest possible interface between the tantalum implant and the host bone, should be met and thus, bone cement and autologous bone grafts should be used with caution.