Controllable synthesis of highly conductive polyaniline coated silica nanoparticles using self-stabilized dispersion
Minkyu Kim1, Sunghun Cho, Jooyoung Song
1WCU program of Chemical Convergence for Energy and Environment (C2E2), School of Chemical and Biological Engineering, College of Engineering, Seoul National University, 599 Gwanak-ro, Gwanak-gu, Seoul 151-742, Korea.
Abstract:
Highly conductive silica/polyaniline (PANi) core/shell nanoparticles (NPs) were synthesized in various diameters (from 18 to 130 nm) using self-stabilized dispersion polymerization. The polymerization was carried out in an aqueous/organic liquid system at -30 °C. In this system, the organic phase plays a key role in directing para-direction oriented polymerization of the PANi on the surface of silica NPs. Because of its para-direction polymerized structure, the synthesized silica/PANi core/shell NPs exhibited enhanced electrical conductivity (25.6 S cm(-1)) compared with NPs (1.4 S cm(-1)) prepared by homogeneous polymerization. The conductivities and BET surface areas were 25.6 S cm(-1)/170 m(2) g(-1) (18 nm in diameter), 22.5 S cm(-1)/111 m(2) g(-1) (35 nm in diameter), 18.3 S cm(-1)/78 m(2) g(-1) (63 nm in diameter), and 16.4 S cm(-1)/53 m(2) g(-1) (130 nm in diameter). In this series, increased para-coupling along the polymer backbone was elucidated using several characterization techniques, including Fourier transform infrared (FTIR), X-ray diffraction (XRD), and nuclear magnetic resonance (NMR) spectroscopy. As-prepared silica/PANi core/shell NPs exhibited capacitance as high as 305 F g(-1).