Nanodomain structures with hierarchical inhomogeneities in PMN-PT

The nanometric domain configuration of (1 - x) Pb(Mg(1/3)Nb(2/3))O(3-x)PbTiO(3) [(1 - x)PMN-xPT] single crystals in the monoclinic phase around a morphotropic phase boundary (MPB) has been examined thoroughly by means of transmission electron microscopy (TEM). Domain structures with hierarchically inhomogeneous configuration were found in the monoclinic phase near the MPB region around x ~ 0.32, which are characterized as nanoscaled lamella-type domain structures with ~10 nm width inside macroscopic-sized banded domains with 100 to 200 nm width. To elucidate formation processes of the domain structures with hierarchically inhomogeneous configuration, an in situ TEM observation of changes of the domain structures in the temperature window between 298K and 500K was carried out. It is revealed that these nanoscaled lamella-type domain structures with ~10 nm width appear inside the banded domains as a result of the tetragonal structure and are inherent to the monoclinic phase.