Fabrication of large domain crack-free colloidal crystal heterostructures with superposition bandgaps using...

An improved convective self-assembly method was developed to fabricate crack-free colloidal crystal heterostructure over a relatively large area. A composite opaline heterostructure composed of polystyrene (PS) colloids was first fabricated. Subsequent calcination of the opaline heterostructure led to the formation of inverse opaline heterostructure composed of SiO(2) or TiO(2). Both opaline and inverse opaline heterostructures demonstrated long-range ordering in a relatively large domain (>100 × 100 μm(2)). Optical reflection measurements of the inverse opaline heterostructures showed dual stop bands as a consequence of the superposition of the stop bands from the individual compositional colloidal crystals (CCs). In addition, the relative position of the two stop bands can be adjusted by varying the size of the colloidal spheres in the original CCs template. Both types of colloidal crystal heterostructures can be used for optical filters, high-efficiency back-reflectors or electrodes in solar cells, differential drug release, and protein patterning.