Physicochemical properties of endodontic sealers of different bases
Gabriela Alexandra Marín-Bauza1, Yara Teresinha Correa Silva-Sousa, Suely Aparecida da Cunha
1School of Dentistry, University of Ribeirão Preto, Ribeirão Preto, SP, Brazil.
Objective:
To assess the setting time (ST), flow (FL), radiopacity (RD), solubility (SB) and dimensional change following setting (DC) of different sealers (AH Plus®, Polifil, Apexit Plus®, Sealapex®, Endométhasone® and Endofill®) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57.
Material And Methods:
Five samples of each material were used for each test. For ST, cast rings were filled with sealers and tested with a Gilmore needle. For FL, the sealer was placed on a glass plate. After 180 s, another plate with 20 g and a load of 100 g were applied on the material, and the diameters of the discs formed were measured. In RD, circular molds were filled with the sealers, radiographed and analyzed using Digora software. For SB, circular molds were filled with the sealers, a nylon thread was placed inside the material and another glass plate was positioned on the set, pressed and stored at 37°C. Samples were weighed, placed in water, dried and reweighed. The water used for SB was analyzed by atomic absorption spectrometry. For DC, circular molds were filled with the sealers, covered by glass plates and stored at 37°C. Samples were measured and stored in water for 30 days. After this period, they were dryed and measured again.
Results:
Regarding ST, AH Plus®, Apexit® and Endofil® sealers are in accordance with ANSI/ADA standards. Endométhasone's manufacturer did not mention the ST; Polifil is an experimental sealer and Sealapex® did not set. Considering RD, SB and DC, all sealers were in accordance with ANSI/ADA. The spectrometric analysis showed that a significant amount of K+ and Zn2+ ions was released from Apexit Plus® and Endofill®, respectively.
Conclusion:
Except for DC, all other physicochemical properties of the tested sealers conformed to ANSI/ADA requirements.
Related Concept Videos
01:19Physical Properties of Carboxylic Acid Derivatives
Among the carboxylic acid derivatives, the boiling points of acid chlorides and esters are very similar and are the lowest in the series. Acid anhydrides have slightly higher boiling...
01:18Titration of Polyprotic Base with a Strong Acid
02:11Leveling Effect and Non-Aqueous Acid-Base Solutions
The Leveling Effect of a Solvent
A generic acid (HA) reacts with the generic base (B-) to yield the corresponding conjugate base (A-) and conjugate acid (HB):
02:35Acid and Bases: Ka, pKa, and Relative Strengths
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
00:53Extraction: Effects of pH