Ligand-Mediated Nucleation and Growth of Palladium Metal Nanoparticles
Published on: June 25, 2018
On the influence of diphosphine ligands on the chemical order in small RuPt nanoparticles: combined structural and
Patricia Lara1, Tuğçe Ayvalı, Marie-José Casanove
1CNRS, LCC (Laboratoire de Chimie de Coordination), 205, Route de Narbonne, F-31077 Toulouse, France.
Abstract:
Diphenylphosphinobutane (dppb) stabilized bimetallic RuPt nanoparticles were prepared by co-decomposition of [Ru(COD)(COT)] [(1,5-cyclooctadiene)(1,3,5-cyclooctatriene)ruthenium] and [Pt(CH(3))(2)(COD)] [dimethyl(1,5-cyclooctadiene) platinum(II)] organometallic precursors under mild conditions (room temperature, 3 bar of dihydrogen) and in the presence of dppb. The determination of the nanoparticles' chemical composition was made possible thanks to a combination of several characterization techniques (HREM, STEM-HAADF, WAXS, EXAFS, IR, NMR) associated with surface reactivity studies based on simple catalytic reactions. The obtained nanoparticles display a ruthenium rich core and a disordered shell containing both ruthenium and platinum. The results were compared with those obtained on nanoparticles of similar size and composition but not containing ligands. The complexity observed in the present structure of these nanoparticles arises from the high chemical affinity of the diphosphine ligand used as a stabilizer for both metals.
More Related Videos
07:14Experimental Approaches for the Synthesis of Low-Valent Metal-Organic Frameworks from Multitopic Phosphine Linkers
Published on: May 12, 2023
12:08Catalytic Reactions at Amine-Stabilized and Ligand-Free Platinum Nanoparticles Supported on Titania During Hydrogenation of Alkenes and Aldehydes
Published on: June 24, 2022