The effect of TiO2 and SiO2 nanoparticles on flexural strength of poly (methyl methacrylate) acrylic resins
Ahmad Sodagar1, Abbas Bahador, Safia Khalil
1Department of Orthodontics, Faculty of Dentistry, Tehran University of Medical Sciences, Tehran, Iran.
Purpose:
TiO(2) and SiO(2) nanoparticles are products of nanotechnology which have been incorporated to acrylic resins (AR) in order to induce antimicrobial properties. However, as additives they can affect the mechanical properties of the final product. The aim of this study was to survey the effects of TiO(2) and SiO(2) nanoparticles on flexural strength (Fs) of poly (methyl methacrylate) acrylic resins.
Methods:
Acrylic specimens (Selecta Plus) in size of 5×10 (±0.2)×3.3 (±0.2)mm were prepared and divided into 7 groups: AR containing nanoTiO(2), SiO(2) and TiO(2) with SiO(2) in two concentration of 1% and 0.5%, in addition to a control group. To prepare nano AR, nanoparticles were added to the monomer. All specimens were stored in 37°C distilled water and underwent Fs test by universal testing machine (Zwick).
Results:
The maximum mean flexural strength (43.5 MPa) belongs to the control group and AR containing 0.5% of both TiO(2) and SiO(2) demonstrated the minimum mean Fs (30.1 MPa). Resins contained TiO(2), demonstrated lower values of Fs than those contained SiO(2) with the same concentration, but the differences were not significant (P>0.05).
Conclusion:
Incorporation of TiO(2) and SiO(2) nanoparticles into acrylic resins can adversely affect the flexural strength of the final products, and this effect is directly correlated with the concentration of nanoparticles.