Synthesis and characterization of polyaniline/Ag-Pt nanocomposite for improved antibacterial activity
Pandi Boomi1, Halliah Gurumallesh Prabu, Jayaraman Mathiyarasu
1Department of Industrial Chemistry, School of Chemical Sciences, Alagappa University, Karaikudi 630003, Tamilnadu, India. pboomi1983@gmail.com
Abstract:
Polyaniline, polyaniline/Ag-Pt nanocomposite and bimetal (Ag-Pt) colloidal solution were chemically synthesized and characterized by UV-vis, XRD, FT-IR, TGA, HRSEM with EDAX and HRTEM techniques. The results reveal that there was a strong interaction between Ag-Pt nanocomposite and polyaniline chains. This interaction makes only small changes in the backbone chain of polyaniline/Ag-Pt nanocomposite when compared with polyaniline. TGA result revealed greater thermal stability of the composite. HRSEM images showed pebble like morphology for polyaniline/Ag-Pt nanocomposite. The average grain size of Ag-Pt nanoparticle was found to be 2-5 nm, which is confirmed by HRTEM analysis. The polyaniline and polyaniline/Ag-Pt nanocomposite were tested for antibacterial activity. The composite showed improved inhibition efficiency with a maximum zone diameter of 30 ± 1.25 mm against Staphylococcus aureus. This is the first report on the synthesis and its antibacterial activity of polyaniline/Ag-Pt nanocomposite.