Repeated bonding of fixed retainer increases the risk of enamel fracture

The aim of this study was to investigate the influences of repeated bonding, using 2 different orthodontic adhesive systems, on the shear bond strength (SBS) and the enamel surface morphology. Sixty premolars were divided into 2 groups (n = 30), and either Transbond XT (T group) or Fuji Ortho LC (F group) adhesives were used. SBS was measured 24 h after bonding, using a universal testing machine. Then, the enamel surfaces were investigated and the mode of failure was described using adhesive remnant index (ARI) scores. After each debonding, 10 teeth from each group were examined by scanning electron microscopy to determine the penetration of adhesives, the length of resin tags, and the state of the enamel surface. The other teeth were subjected to two more bonding/debonding procedures. In T group, the second debonding sequences had significantly higher bond strengths than the other sequences. The length of resin tags was greatest in the second debonding sequence, although there was no significant difference. In F group, the SBS increased with further rebonding and the failure mode tended towards cohesive failure. In both groups, the ARI scores increased with rebonding. Enamel loss could have occurred with both adhesives, although the surfaces appeared unchanged to the naked eye. From this study, we suggest that enamel damage caused by repeated bonding is of concern. To prevent bond failure, we should pay attention to the adhesion method used for bondable retainers.