Discoloration of titanium alloy in acidic saline solutions with peroxide

Shinji Takemoto1, Masayuki Hattori, Masao Yoshinari

  • 1Department of Dental Materials Science, Tokyo Dental College, Mihama-ku, Chiba, Japan. takemoto@tdc.ac.jp

Dental Materials Journal
|February 2, 2013
PubMed

More Related Videos

Platelet-Derived Extracellular Vesicle Functionalization of Ti Implants04:16

Platelet-Derived Extracellular Vesicle Functionalization of Ti Implants

Published on: August 5, 2021

Plasma Polishing as a New Polishing Option to Reduce the Surface Roughness of Porous Titanium Alloy for 3D Printing06:12

Plasma Polishing as a New Polishing Option to Reduce the Surface Roughness of Porous Titanium Alloy for 3D Printing

Published on: April 28, 2023

Related Concept Videos

Oxidations of Aldehydes and Ketones to Carboxylic Acids01:15

Oxidations of Aldehydes and Ketones to Carboxylic Acids

Oxidation of aldehydes and ketones results in the formation of carboxylic acids. Aldehydes, bearing hydrogen next to the carbonyl group, are easily oxidized compared to ketones. This is because an aldehydic proton can easily be abstracted during oxidation.
Aldehydes readily undergo oxidation in strong oxidizing agents such as potassium permanganate and chromic acid. The oxidation can also be carried out using mild oxidizing agents such as silver oxide. In fact, aldehydes can be easily oxidized...
Effects of EDTA on End-Point Detection Methods01:18

Effects of EDTA on End-Point Detection Methods

Different methods, such as visual observance of metal-ion indicators, spectroscopic techniques, and potentiometric methods, can determine the endpoint of an EDTA titration.
In the visual method, metal-ion indicators (metallochromic dyes), which have distinct colors in their free and complex forms, are added to the mixture to signal the titration's end point. They form stable complexes with metal ions, but these complexes are weaker than the corresponding metal–EDTA complexes. As a result, EDTA...
Acid Mine Drainage01:19

Acid Mine Drainage

Mining activities that disturb sulfide-rich rocks, particularly those containing pyrite (FeS₂), initiate a cascade of geochemical and microbiological processes with serious environmental implications. When exposed to air and water, pyrite undergoes oxidation, releasing sulfate, ultimately forming sulfuric acid and mobilizing heavy metals into surrounding water systems. This phenomenon, known as acid mine drainage (AMD), results in low pH waters laden with toxic elements that threaten aquatic...
Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
Microbial Corrosion01:24

Microbial Corrosion

Microbiologically Influenced Corrosion (MIC) is a significant form of material degradation caused by the metabolic activities of microorganisms. This phenomenon poses substantial challenges across various industries, including oil and gas, maritime, and water treatment sectors.MIC occurs when microorganisms, such as bacteria, archaea, and fungi, colonize metal surfaces, forming biofilms that alter the local electrochemical environment. These biofilms can lead to the production of corrosive...
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...