Formulation of Diblock Polymeric Nanoparticles through Nanoprecipitation Technique
Published on: September 20, 2011
Poly ɛ-caprolactone nanoparticles loaded with Uncaria tomentosa extract: preparation, characterization, and
Ana Ferreira Ribeiro1, Ricardo Leite de Oliveira Rezende, Lúcio Mendes Cabral
1Department of Pharmaceutics, Federal University of Rio de Janeiro, Rio de Janeiro, Brazil.
Purpose:
The aim of this research was to develop and optimize a process for obtaining poly ɛ-caprolactone (PCL) nanoparticles loaded with Uncaria tomentosa (UT) extract.
Methods:
Nanoparticles were produced by the oil-in-water emulsion solvent evaporation method. Preliminary experiments determined the initial conditions of the organic phase (OP) and of the aqueous phase (AP) that would be utilized for this study. Ultimately, a three-factor three-level Box-Behnken design (BBD) was employed during the optimization process. PCL and polyvinyl alcohol (PVA) concentrations (X(1) and X(2), respectively) and the AP/OP volume ratio (X(3)) were the independent variables studied, while entrapment efficiency (Y(1)), particle mean diameter (Y(2)), polydispersity (Y(3)), and zeta potential (Y(4)) served as the evaluated responses.
Results:
PRELIMINARY EXPERIMENTS REVEALED THAT THE OPTIMAL INITIAL CONDITIONS FOR THE PREPARATION OF NANOPARTICLES WERE AS FOLLOWS: OP composed of 5 mL ethyl acetate/acetone (3/2) mixture containing UT extract and PCL, and an AP of buffered PVA (pH 7.5) solution. Statistical analysis of the BBD results indicated that all of the studied factors had significant effects on the responses Y(1), Y(2), and Y(4,) and these effects are closely described or fitted by regression equations. Based on the obtained models and the selected desirability function, the nanoparticles were optimized to maximize Y(1) and minimize Y(2). These optimal conditions were achieved using 3% (w/v) PCL, 1% (w/v) PVA, and an AP/OP ratio of 1.7, with predicted values of 89.1% for Y(1) and 280 nm for Y(2). Another batch was produced under the same optimal conditions. The entrapment efficiency of this new batch was measured at 81.6% (Y(1)) and the particles had a mean size of 247 nm (Y(2)) and a polydispersity index of 0.062 (Y(3)).
Conclusion:
This investigation obtained UT-loaded nanoparticle formulations with desired characteristics. The BBD approach was a useful tool for nanoparticle development and optimization, and thus should be useful especially in the realm of phytotherapeutics, in which varied compositions may be assessed in quantitative and qualitative terms.