Effect of various laser irradiations on the mineral content of dentin
Erhan Dilber1, Meral Arslan Malkoc, A Nilgun Ozturk
1Department of Prosthodontics, Faculty of Dentistry, Sifa University, Izmir, TURKIYE.
Objective:
THE AIM OF THIS STUDY WAS TO EVALUATE THE MINERAL CONTENT OF DENTIN IRRADIATION WITH ERBIUM: yttrium-aliminum-garnet (Er:YAG), Neodmiyum:yttrium-aliminum garnet (Nd:YAG) and potassium titanium phosphate (KTP) laser used for in the treatment of dentin hypersensitivity.
Methods:
Six extracted wisdom, unerupted molar teeth were used in this study. The enamel of the teeth was removed with a conventional bur under water cooling to expose the dentin surface. The teeth were mounted in a slow-speed, diamond-saw, sectioning machine. Two dentin slabs were obtained from each tooth and each slab was sectioned so that 4 slabs were made from each teeth. Then dentin slabs were randomly divided into four groups. Group A: Control Group, Group B: Er:YAG laser, Group C: Nd:YAG laser, Group D: KTP laser. The levels of Ca, K, Mg, Na,P and Ca/P mineral ratio in each dentin slab were measured by inductively coupled plasma-atomic emission spectrometry (ICP-AES). Data were analysed by one way analysis of variance (ANOVA) and Tukey HSD tests. One sample from each group was prepared for scanning electron microscopy (SEM).
Results:
There were no significant differences between the groups for Ca, K, Mg, Na,P and Ca/P mineral ratio (P>.05). SEM photographs indicated that there were melted areas around the exposed dentin tubules in groups treated with Er:YAG and KTP lasers.
Conclusion:
This study demonstrated that laser etching with the Er:YAG, Nd:YAG, KTP laser systems did not affect the compositional structure of the dentin surfaces.