Robust superamphiphobic film from electrospun TiO2 nanostructures

Rice-shaped TiO2 nanostructures are fabricated by electrospinning for creating a robust superamphiphobic coating on glass substrates. The as-fabricated TiO2 nanostructures (sintered at 500 °C) are superhydrophilic in nature which upon silanization turn into superamphiphobic surface with surface contact angle (SCA) values achieved using water (surface tension, γ = 72.1 mN/m) and hexadecane (surface tension, γ = 27.5 mN/m) being 166° and 138.5°, respectively. The contact angle hysteresis for the droplet of water and hexadecane are measured to be 2 and 12°, respectively. Thus, we have successfully fabricated superior self-cleaning coatings that possess exceptional superamphiphobic property by employing a simple, cost-effective, and scalable technique called electrospinning. Furthermore, the coating showed good mechanical and thermal stability with strong adherence to glass surface, thus revealing the potential for real applications.