Extending the limits of precision polymer synthesis: giant polyphenylene dendrimers in the megadalton mass range

Thi-Thanh-Tam Nguyen1, Martin Baumgarten, Ali Rouhanipour

  • 1Max Planck Institute for Polymer Research, Ackermannweg 10, D-55128 Mainz, Germany.

Journal of the American Chemical Society
|March 5, 2013
PubMed

More Related Videos

MALDI-ToF MS Method for the Characterization of Synthetic Polymers with Varying Dispersity and End Groups06:16

MALDI-ToF MS Method for the Characterization of Synthetic Polymers with Varying Dispersity and End Groups

Published on: October 3, 2025

Synthesis of Cyclic Polymers and Characterization of Their Diffusive Motion in the Melt State at the Single Molecule Level06:55

Synthesis of Cyclic Polymers and Characterization of Their Diffusive Motion in the Melt State at the Single Molecule Level

Published on: September 26, 2016

Related Concept Videos

Determination of Molar Masses of Polymers I01:24

Determination of Molar Masses of Polymers I

Polymerization produces macromolecules with a range of chain lengths due to the random nature of molecular growth processes. As chains form and terminate at different stages, a single polymer sample contains molecules of varying sizes rather than a uniform structure. This variability is described using average molar masses and distribution-related parameters, which together provide a comprehensive understanding of polymer characteristics.The distribution of molar masses plays a critical role in...
Molecular Weight of Step-Growth Polymers01:08

Molecular Weight of Step-Growth Polymers

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...
Ziegler–Natta Chain-Growth Polymerization: Overview01:17

Ziegler–Natta Chain-Growth Polymerization: Overview

Ziegler–Natta polymerization is another form of addition or chain‐growth polymerization used for synthesizing linear polymers over branched polymers. The catalyst used for polymerization is the Ziegler–Natta catalyst, named after Karl Ziegler and Giulio Natta, who developed it in 1953. This catalyst is an organometallic complex of titanium tetrachloride and triethyl aluminum, with the active form of the catalyst being an alkyl titanium compound. Using the Ziegler–Natta catalyst, high molecular...
Step-Growth Polymerization: Overview01:03

Step-Growth Polymerization: Overview

Step-growth or condensation polymerization is a stepwise reaction of bi or multifunctional monomers to form long-chain polymers. As all the monomers are reactive, most of the monomers are consumed at the early stages of the reaction to form small chains of reactive oligomers, which then combine to form long polymer chains in the late stages. Hence, the reaction has to proceed for a long time to achieve high molecular weight polymers.
Many natural and synthetic polymers are produced by...
Polymers: Molecular Weight Distribution01:10

Polymers: Molecular Weight Distribution

For any given polymer, the weight average molecular weight (Mw) is higher than, if not equal to, the number average molecular weight (Mn). The only situation in which the weight average molecular weight and the number average molecular weight are equal is when a polymer consists only of chains with equal molecular weight. However, this never happens in a synthetic polymer, since it is difficult to control the polymerization process up to a molecular level with accuracy to a hundred percent.
Radical Chain-Growth Polymerization: Chain Branching01:17

Radical Chain-Growth Polymerization: Chain Branching

The skeletal structure of polymers synthesized via radical polymerization is always branched. For example, the polymerization of ethylene by radical polymerization results in a low-density grade of polyethylene with a heavily branched skeletal structure. Here, the radical site abstracts hydrogen from the growing chain, and the radical site shifts from the end (a primary carbon center) to anywhere within the growing chain (a secondary carbon center). Consequently, the part of the chain from the...